An ar coating maximizes the transmission over 3 to 5 µm r avg 2.
Barium fluoride optical windows.
For an equivalent thickness the transmission extends approximately 1 micron further into the ir than calcium fluoride.
Barium fluoride baf is also a scintillation material that exhibits one of the fastest known decay constants among inorganic materials.
While barium fluoride windows are less resistant to water than calcium fluoride baf 2 windows are the most resistant optical fluoride to high energy radiation but feature lower uv.
Although these windows are ar coated on both sides for ir use barium fluoride is commonly chosen for applications that require transmission into the ultraviolet.
Baf2 has excellent transmission from 200nm 12μm and resistance to high energy radiation.
Barium fluoride is used for optical windows prisms and lenses transmitting from ultraviolet into infrared it can be used as an infrared laser window or lens.
Barium fluoride is often suitable for applications in the passive ir band 8 to 14 μm and is often used as a viewport window for thermography.
Barium fluoride baf2 lenses windows mirrors filters and prisms.
Windows intended primarily for ir use and noted as having ir polish may have.
Barium fluoride windows can be used up to 800 c in a dry environment but prolonged exposure to moisture can degrade transmission in the vacuum ultraviolet range.
Thorlabs barium fluoride baf 2 precision windows are available in ø1 2 and ø1 sizes.
Barium fluoride is resistant to high energy radiation performing well in dry temperatures up to 800 c but transmission in the vacuum uv vuv degrades over time in a moist atmosphere and the material is susceptible to water corrosion at 500 c.
Barium fluoride baf2 windows.
Barium fluoride baf is a crystalline compound of barium and fluoride used in optical applications in the nir vis and mwir spectrums.
Baf 2 is recommended for use as a vacuum ultraviolet window where high radiation resistance is required.